Our powder bed selective electron beam melting 3D printing system – T200 is suitable for low-cost rapid printing and forming with the metal powders, such as Ti6Al4V(TC4), Ti600, TiAl intermetallic compounds, copper alloys, stainless steel, high-temperature alloys, refractory metals, high entropy alloys, hard alloys and other materials. The main technical characteristics are as follows:

• Equipped with a high-power and long-life intermittent heating electronic gun, it can quickly preheat a powder bed with a width of 200mm x 200 mm to above 1100 ℃ to achieve the higher dimensional accuracy of formed parts;
• Forming in a vacuum environment results in higher purity and cleanliness of the formed parts;
• The maximum power is 6kW, with higher energy absorption and utilization efficiency (electron beam to material);
• The powder bed temperature is ≥ 1100 ℃, which allows the printed parts to have lower forming thermal stress and residual stress;
• More formable materials, including but not limited to Ti6Al4V(TC4), Ti600, TiAl intermetallic compounds, copper alloys, stainless steel, high-temperature alloys, refractory metals, high entropy alloys, hard alloys, etc.
• The up-to-down powder feeding method is applied, so the powder quantity in the powder bin can be detected in real time;
• Equipped with brand new powder recycling equipment, the powder removing process after printing is more efficient and convenient;
• Our SEBM printing system with independent intellectual property rights can independently adjust process parameters to adapt to the development of different material forming processes.